QINGDAO YOSION LABTECH CO., LTD. | Updated: Aug 28, 2016


Product Detail

Basic Info
  • Model NO.:SJ101

  • state:Solid

  • pH:Alkaline

  • Type:Inorganic

  • Melting Point:>600℃

  • Chemical Composition:SiO₂=10%-30%

  • Function:Protect Weld Metal

  • Application:Submerged-arc Welding

  • Manufacturing Method:Sintering

  • Accompanied Wire:H08mna / H08mnmoa

  • Flux Type:Asoda-Fluorine

  • Alkalinity:About 1.8

  • Current:AC or DC

  • Applications:Welidng Low Carboon Steel, Low Alloy Steel

  • Production Name:Sintered Flux Sj101

  • Trademark:OEM

  • Specification:CE, NGV

  • Origin:Qingdao, China

  • HS Code:381090000

Product Description
China Wedling Materials Manufacturer Yu Lin Brand Saw Flux SJ101

YULIN Brand sintering welding flux has steady arc , nice weld formation , and easy in slag removing , as well with perfect deposit metal mechanical properties .
YULIN Brand sintering welding flux is widely applied in large domestic and abroad steel structure ,spiral pipe , tube and power seam boiler and pressure vessel , chemical , ship building , motorcycle , cars , railway bridge ,oil transportation lines,etc .

According to : GB/T5293 F4A4-H08MnA
                     F5A4-H10Mn2
             GB/T12470F55A4-WGX2
Equal to : AWS / ASME SFA-5.17F7A4-EH14

Parameter introduction of Sintered Flux SJ101
Brand :YULINClassification:Soda-fluorine type
AlkalinityAbout 1.8Grain Size:10-60

Feature of Yu Lin Brand Saw Flux SJ101
1: It can be operated with AC and DC .
2: Good desulfurization and dephosphorization ability .
3:Strong anti rust ability
4: Steady arc ,nice welding appearance and easy in slag removing .
5:Better resist cold , heat crack properties

Applications of Yu Lin Brand Saw Flux SJ101
1:Accompanying suitable wires (H08MnA , H08MnMoA , H08Mn2MoA ,H10Mn2 ,etc .) ,
2:mainly applied in the fast welding of low carbon steel and some low alloy steel structure ( like 16Mn, X65, X70, 14Mn Niq, Q345C ,etc. ) and submerged welding of boiler pressure vessels , ships , bridges , oil transportation lines ,etc .
3: SJ101 also can be used for welding the thick-walled structure different grade high strength steel .

Chemical Composition (%) of Yu Lin Brand Saw Flux SJ101
SiO 2 +TiO 2CaO+MgOAl 2 O 3 +MnOCaF 2SP
20~3025~3515~3015~25≤0.06≤0.08
Mechanical Properties of Deposited Metal Yu Lin Brand Saw Flux SJ101
Accompanied
Wires
Yield Strength
(δ s) Mpa
Tensile Strength
(δ b ) Mpa
Elongation
A(δ 5) %
Charpy - V impact Test (J)
-20ºC-30ºC-40ºC

HO8MnA
≥330415~550≥22≥47≥37≥37
H10Mn2≥400480~650≥22≥47≥37≥37
Notice :

1.Before welding , should remove the rust, oil , water and other impurities from the welding surface .
2. The welding flux should be dried 2 hours in 300-350ºC .

Product specification/models: SJ101, SJ101G,SJ101Q, SJ301, SJ301A, SJ501, SJ601,HJ350,HJ431.

If you want to get better welding results , if you want to save 20% of the welding flux ,if you want to find a high quality welding materials factory , pls contact us as soon as possible .
0086-18037375378 . let's chat on line at any time.
Contact us :
Roise Du
 
 
 
WEB:www.yulinflux.com
China Wedling Materials Manufacturer Yu Lin Brand Saw Flux SJ101

                                 


Contact Us

Qingdao Yosion Labtech Co.,Ltd

ADD: No.506 South Shanghai Road, Huangdao District(Jiaonan), Qingdao City

Phone: +8618266641751

Phone: +86-532-83978550

fax: +86-532-83978550

E-mail: annezhang@yosionlabtech.com

Skype: annezhang@yosionlabtech.com

Wbsite:www.yosionlabtech.com  / www.yosionlabtech.com.cn

Copyright © QINGDAO YOSION LABTECH CO., LTD.
Tel: +86-532-83978550
Fax:+86-532-83978550
E-mail:amyli@yosionlabtech.com
Address:No.506 South Shanghai Road,Huangdao District(Jiaonan),Qingdao City,Shangdong,China